The FiloSlim P2662 is a cold-curing two-component polyurethane resin developed for cable joints up to 10 kV. The resin is composed of polyether polyols, ester polyols and has fire retardant properties. This resin has been specially developed for use in the FiloSlim cable joint.
The moisture resistant formula P2662 is classified as L-R-W classified (Low Voltage - Rigid - Suitable for applications in presence of Water) according to IEC 60455-3-8:2013.
The FiloSlim resin packaging is equipped with an integrated filling nipple. After mixing the resin, the package is placed on the injection valve and opened by turning it a quarter turn. The packaging is now linked to the injection valve and can be easily emptied into the cable joint with manual force.
When the cable joint is filled, the packaging can be removed by turning it a quarter turn back. The injection valve and the resin packaging will be closed completely liquid-tight with this simple operation. A partially used resin package can be used for a next joint.
|Potlife (process time)|
|0.3 l at 5°C||minutes||34||IEC 60455-2|
|0.3 l at 40°C||minutes||7.5||IEC 60455-2|
|Density||g/cm³||1.2||EN ISO 1183-1|
|Impact strength||kJ/m²||33.8 (no break)||EN ISO 179|
|Hardness||Shore D||41||EN ISO 868|
|Tensile strength||MPa||8.29||EN ISO 527|
|Elongation at break||%||112||EN ISO 527|
|Curing in the presence of water - Gas volume||ml||0||IEC 60455-2|
|Volume resistivity at room temperature||Ohm||1,1x10¹⁵||IEC 60093|
|Dielectric strength at room temperature||kV/mm||>20 kV/mm||EN 60243-1|
|Temperature resistance||°C||-25 tot +120|
|Dry heat resistance: 28 days at 120°C||IEC 60455-2|
|Mass loss||%||2.89||HD 631.1 S2: 2007-12|
|Impact strength||kJ/m²||23.7||EN ISO 179|
|Wet heat resistance: 28 days at 90°C||IEC 60455-2|
|Hardness (retention/original)||%||85||EN ISO 868|
|Tensile strength (retention/original)||%||85.5||EN ISO 527|
|Elongation at break (retention/original)||%||122||EN ISO 527|
|Dielectric strength||kV/mm||18.1||EN 60243-1|